Effect of Humic Acid Binder on Oxidation Roasting of Vanadium–Titanium Magnetite Pellets via Straight-Grate Process

Abstract

The oxidation roasting of vanadium–titanium magnetite (VTM) pellets with a new composite binder was investigated using a pilot-scale straight-grate. The evolution of the chemical and phase composition, the compressive strength, and the metallurgical properties of the fired VTM pellets were investigated. Under a preheating temperature of 950 ∘C, a preheating time of 18 min, a firing temperature of 1300 ∘C, and a firing time of 10 min, the compressive strength of the fired pellets was as high as 2344 N per pellet. The fired pellets mainly consisted of hematite, pseudobrookite, spinel and olivine. The total iron content of the fired pellets was 0.97% higher using 0.75 wt% humic acid (HA) binder instead of 1.5 wt% bentonite binder. These properties are beneficial for the production efficiency and energy efficiency of their subsequent use in blast furnaces. Moreover, both the softening interval and the softening melting interval of the HA binder pellets were narrower than those of the bentonite binder pellets, conducive to the smooth and successful smelting of the VTM pellets in a blast furnace.

Keywords

• humic acid binder
• oxidation roasting
• vanadium-titanium magnetite pellets
• straight-grate process