Chemical, thermal and viscous characterization of high-oleic sunflower and olive pomace acid oils and derived estolides

Abstract

This work deals with the chemical, thermal and viscous characterization of a variety of estolides, prepared from higholeic sunflower and olive pomace acid oils, using different acid-catalyzed synthesis protocols and reaction times. Estolides with weight-average molecular weights between 1.7 and 3.4 times higher than the original acid oils were obtained. The molecular weight of the estolides was higher when using the sulphuric acid-catalyzed method and a reaction time of 3-6 h. Estolides presented higher freezing temperatures than acid oils. In general, viscosity values are related to estolide molecular weight. Significant increments in viscosities were found in comparison with acid oils. Maximum viscosity values were obtained for estolides prepared using the sulphuric acidcatalyzed method. The largest viscosity increments in olive pomace acid oil-derived estolides were observed during the first 6 hours of reaction, due to an increase in the molecular weight; longer reaction times yielded adverse results. The temperature dependence of viscosity for all estolides studied is significantly larger than for the original acid oils.

Keywords

• biolubricants
• byproducts
• estolides
• high-oleic sunflower acid oil
• olive pomace acid oil
• thermal analysis
• viscosity